Roxil 2-Part Wood Filler

Carry out repairs within one hour with this all-in-one rapid-curing polyester resin wood filler kit. Contains filler, activator, spatula and mixing bowl — everything you need to repair damaged timber. Flexible paste for application to wood holes, cracks and other defects. Roxil 2-Part Wood Filler can be planed, carved or sanded for a seamless finish once cured. Results in a stainable and paintable surface for a blemish-free fix. Perfect for repair following a complete rot treatment.

Mould and Sand Just Like Real Wood in Natural or White Colours

Roxil Wood 2-Part Filler is easy to work with and adheres strongly to wood.

Easily build up multiple layers for large-scale repairs and sand within 30 minutes of application.

Simple enough for amateur use and strong enough for professional repairs.

Choose Natural to blend into light-coloured woods like maple, ash or pine. Choose white for best results on overpainted surfaces. Both colours are compatible with high opacity, premium paints and solvent-based wood stains.

Drillable Crack-Resistant & Styrene-Free Filler

Hang photo frames, mirrors and more after repair.

Once cured, Roxil 2-Part Wood Filler is strong enough to hold screws and nails in place.

It can also be used to repair damaged screw or nail holes.

Competing wood fillers are styrene-based – a carcinogen and environmental hazard.

Roxil 2-Part Wood Filler is styrene-free. Manufactured using a vacuum production process that ensures every pack delivers a smooth, air bubble-free material.

Compatible With the Roxil Wood Protection Range

Use Roxil 2-Part Wood Filler to repair defects and damage in weathered, rot-damaged or reclaimed wood before applying Roxil Wood Protection Cream or Roxil Wood Preserver for a long-lasting waterproof structure.

Product Properties

Appearance	Available in 2 colours: White & Natural
Size(s) & Mixing ratio	50 parts filler to 1 part hardener by weight
Coverage	400 cm3 as supplied
Adhesion to wood	Greater than the cohesive strength of the wood.
Hardening	15 – 20 Minutes @ 20 °C
Mixed density	1.25 g/cm3